스테인레스 강의 특성과 용도

Has lower Cr, Ni content than 304 steel. Its tensile strength increases with cold working. It is non-magnetic but becomes magnetic when cold worked.

기차, 항공기부품, 벨트콘베이어,자동차,볼트,스프링,자동차휘커버

301L is produced by lowering the C content in 301 in order to improve grain boundary corrosion resistance of the welding part. A drop in strength due to reduced C content is reinforced by adding N.

기차프레임,건물외장재

Improved machining by adding S.

가정용품,볼트,너트,기계부품

Most widely used steel type. 304 is known for good corrosion resistance, thermal resistance, low-temperature strength and mechanical properties. 304 has good drawability such as deep drawing and bending. 304 is not hardened by heat treatment. (non-magnetic, usable temperature: -196~800°C)

부엌용품,싱크대,내장용배관,보일러,욕조,자동차부품(와이퍼,머플러,몰딩),의학용계장품,건물자재,화학설비,음식 유제품산업,용기

304L is low carbon 304 steel. Under normal conditions, it has similar corrosion resistance to 304. Excellent resistance to inter-granular corrosion after welding and stress relieving. Has corrosion resistant properties without heat treatment and is generally used at temperatures under 400°C(non-magnetic, usable temperature:-196~800°C)

내구성이 요하는 화학, 석탄, 석유용 기계 및 공구, 내열부품과 열처리가 어려운 부분품용

By adding Cu, it has anti-microbial property and good drawability. Useful for deep drawing products which requires a hygienic environment

보온병,싱크,용기,집단배식설비,문손잡이,방적용

304steel is made by lowering the S and Mn content in 304 steel and adding N to prevent ductility reduction. Strength is improved and thickness reduced.

구조강,가로등,물탱크,물 파이프

Strength and inter-granular corrosion resistance are improved by adding N.

구조강,열교환기,화학용기

Steel types formed for wire rods by adjusting the C content in 304 steel. Strength increases with cold drawing.

H: 와이어로프,후크, CD Bars 
M: mesh, bolts, nuts, CD Bars 
S: mesh

Steel types formed for wire rods by adjusting the C content in 304. Good cold workability and free-cutting property.

HA: shaft 
HC: 중형 및 대형 볼트 및 너트
HD: CD Bars HN: 못

High Ni content. Non-magnetic and suitable for deep drawing use due to good cold formality.

식기류, 전기용품

Excellent corrosion resistance, pitting corrosion resistance and high temperature strength by adding Mo. Useful in severe/harsh conditions. Excellent work hardening (non-magnetic).

해수용기기,화학용기기,종이,염료,비료,사진 및 식품산업 그리고 해안지역 건설용, 로프,CD Bars,너트,볼트

Low carbon steel type. Has the normal properties of 316 plus excellent inter-granular corrosion resistance.

입자경계 부식에 적합

Has 316 steel properties and suitable for ultra fine wire.

Mesh

By adding Ti, prevents intra-granular corrosion, suitable for temperatures between 430°C~900°C

비행기 배기관, 보일러, 열교환기

By adding Ti, 409L has good weldability and drawability.

자동차 배기관, 열교환기, 후열처리가 필요하지 않은 콘테이너

Excellent welding bendability by lowering the C content in 410 steel; high temperature oxidation resistance (magnetic).

기계 프레임, 엔진 배기관, 보일러 연소기, 버너

430 is the basic ferritic steel type. 430 is known for low thermal expansion rate and excellent drawing and oxidation resistance.

내열공구, 버너, 가정용품, 싱크카바, 건물재, 너트,볼트,CD Bars, mesh

Adding Mo,Ti and Nb results in good corrosion resistance, weldability and high temperature oxidation resistance.

세탁기계 드럼,자동차배기관, 전기용품, 3중 라미네이트 용기

Adding Mo,Ti and Nb results in excellent corrosion resistance, drawability and weldability.

자동차 배기관, 온수공급설비

410 is the basic martensite steel type known for its good strength but it is not suitable for uses in harsh/severe corrosion conditions. 410 hardens with heat treatment (magnetic).

일반용도칼, 기계부품, 정유설비부품, 볼트, 너트, 펌프축, 수저, 포크

In quenching condition, has high strength and good corrosion resistance (magnetic)

쪽집게, 부엌칼, 터빈날개

Compared to 420J1, higher post-quenching strength (magnetic).

칼날, 노즐, 밸브, 자, 가위, 일반용 칼

규  격 (Grades)

특        성

용   도

KS

JIS

ASTM

DIN

STS
304

SUS
304

TP
304

1.4301

우수한 내식성, 내열성, 저온인성을 가지며 성형가공성 및
용접성이 양호하다. 열처리에 의해 경화되지 않으며
자성은 없다.

화학공업설비, 식품공업배관, 차량부품,
섬유공업설비, 내열부품, 선박부품, 건축
및 장식, 주방기구, 가정용기기

STS
304L

SUS
304L

TP
304L

1.4306

저탄소의 Ni-Cr강으로 보통상태에서 내식성은 304와 유사
하나 용접 후, 또는 응력제거 열처리 후의 입계부식에 대한
저항이 극히 우수하다.

석유화학공업, 화학섬유공업,
원자력발전설비

STS
316

SUS
316

TP
316

1.4401

2~3% Mo의 첨가와 동시에 Ni함량을 증가시킨 것으로
내식성(특히 황산)이 우수하다. 공식에 대한 저항성이 크고
고온 크리프 강도 및 열처리 강도가 높으며 경화성 및
자성은 없다.

석유화학공업, 합성섬유공업, 화학비료
공업, 제지공업, 식품제조설비

STS
316L

SUS
316L

TP
316L

1.4404

저탄소의 Mo함유 Ni-Cr강으로서 316의 특성과 유사하나
용접 후, 또는 응력제거 열처리 후의 내입계부식성이 우수

제지펄프공업, 화학섬유공업, 염색기계,
인산 등의 제조장치

STS
310S

SUS
310S

TP
310S

1.4845

최고의 Cr%를 가진 오스테나이트계 강종으로서 C의 양을
낮게 하여 내식성을 향상 시킨 것이다.

초산탱크 기타의 화학공업장치 저항기등

STS
430

SUS
430

TP
430

1.4016

Ferrite계의 대표적 강종으로서 양호한 냉간 가공성,
내식성을 갖는다. 열처리 경화성은 없으나 자성은 있다.

가정용 주방기구, 제당공업, 자동차부품
건축, 전기기기